Processo de nitretação em banho de sais atóxicos: obtenção e análise de camadas desenvolvidas em aço baixo carbono

Show simple item record

dc.contributor.advisor Zimmer, Cínthia Gabriely pt_BR
dc.contributor.advisor Zimmer, André pt_BR
dc.contributor.author Bonow, Vinícius Timm pt_BR
dc.date.accessioned 2021-04-01T23:08:02Z pt_BR
dc.date.issued 2020 pt_BR
dc.identifier.uri https://dspace.ifrs.edu.br/xmlui/handle/123456789/243 pt_BR
dc.description.abstract Este trabalho vislumbra uma alternativa que origine menor impacto ambiental, em relação ao processo convencional de nitretação líquida, que utiliza sais contendo cianetos e cianatos. Para tanto, foram analisadas as camadas obtidas em amostras de aço 0,2% de carbono, nitretadas em meio aos sais atóxicos de nitrato de potássio (KNO₃) e nitrito de sódio (NaNO₂), como também adições de sais redutores de óxidos testados com cloreto de sódio (NaCl) e cloreto de potássio (KCl). Caracterizações microestruturais foram realizadas com o auxílio de microscopia óptica e microscopia eletrônica de varredura. A composição da camada foi determinada via espectroscopia dispersiva de energia e a dureza foi verificada por meio de um microdurômetro Vickers. O KNO₃ se mostrou mais eficaz na formação da camada branca, enquanto a adição do KCl exibiu melhor ação desoxidante, favorecendo a formação de uma camada mais espessa. Para a melhor condição estudada, a mistura de 75% KNO₃ e 25% KCl, observou-se a formação de uma camada branca uniforme com 8 µm de espessura, verificando um aumento de dureza, partindo de 198 HV no substrato para 702 HV na superfície. A composição química confirmou a presença de nitrogênio na camada, o que comprova a difusão desse elemento na matriz metálica e a formação de nitretos. Conclui-se que a substituição dos sais convencionais por sais atóxicos se mostrou uma alternativa eficiente, apresentando a vantagem de ser um processo que utiliza matérias-primas ambientalmente amigáveis. pt_BR
dc.description.abstract This work presents a less environmental impact alternative, due to the conventional liquid nitriding process, which uses salts containing cyanides and cyanates. For this purpose, the layers obtained in 0.2% carbon steel nitrided samples were analyzed in the midst of the non-toxic salts of potassium nitrate (KNO₃) and sodium nitrite (NaNO₂), as well as additions of oxide reducing salts tested with chloride sodium (NaCl) and potassium chloride (KCl). Microstructural characterizations were performed with the assist of optical microscopy and scanning electron microscopy. The layer composition was determined via energy dispersive spectroscopy and the hardness was verified using a Vickers microdurometer. KNO₃ was more effective in the formation of the white layer, while the addition of KCl exhibited a better deoxidizing action, favoring the formation of a thicker layer. For the best studied condition, the mixture of 75% KNO₃ and 25% KCl, it was observed the formation of a uniform white layer with 8 µm of thickness, verifying an increase of hardness, starting from 198 HV in the substrate to 702 HV in the surface. The chemical composition confirmed the presence of nitrogen in the layer, which proves the diffusion of this element in the metallic matrix and the formation of nitrides. It is concluded that the replacement of conventional salts with non-toxic salts can be an efficient alternative, with the advantage of being a process that uses environmentally friendly raw materials. en
dc.format.mimetype application/pdf pt_BR
dc.language.iso por pt_BR
dc.rights Open Access en
dc.subject Engenharia de materiais pt_BR
dc.subject Ciência dos materiais pt_BR
dc.title Processo de nitretação em banho de sais atóxicos: obtenção e análise de camadas desenvolvidas em aço baixo carbono pt_BR
dc.type Dissertação pt_BR
dc.degree.grantor Instituto Federal de Educação, Ciência e Tecnologia do Rio Grande do Sul pt_BR
dc.degree.level Mestrado pt_BR
dc.degree.date 2020 pt_BR
dc.degree.local Feliz, BR-RS pt_BR
dc.degree.program Programa de Pós-Graduação em Tecnologia e Engenharia de Materiais pt_BR
dc.degree.department Campus Feliz pt_BR


Files in this item

Files Size Format View Description
123456789243.pdf 16.08Mb PDF View/Open Texto completo

This item appears in the following Collection(s)

Show simple item record

Search DSpace


Browse

My Account